Originální podložky Nord-Lock

Společnost Nord-Lock vytvořila originální technologii jištění na principu závěrného klínu, která zajišťuje šroubové spoje, a to i při vystavení silným vibracím a dynamickým zatížením. Není možné, aby se naše výrobky samovolně uvolnily kvůli klínu vytvořenému pod hlavou šroubu a maticí.

Nord-Lock Steel Washers

Applications General steel applications
Material standard EN 1.7182
Size range M3-M130
#5 to 5"
Corrosion resistance Minimum 1,000 hours in salt spray test (according to ISO 9227)
Hardening Through hardened
Washer hardness* ≥ 465HV1
Coating Delta Protekt® KL100 zinc flake coating
Bolt grades Up to 12.9
Temperature range*** -50°C to 200°C
Product designation NL
NLsp
Laser marking type code flZn

 

* Washer hardness must be greater than the hardness of the mating surfaces in order to assure its mechanical function.

*** Temperature recommendations are based on information from the raw material supplier and testing. The locking function is not affected within the specified range.

Nord-Lock Stainless Steel Washers

Applications General stainless steel applications
Material standard EN 1.4404
Size range M3-M80 
#5 to 3 1/8"
Corrosion resistance PREN 27**
Hardening Surface hardened
Washer hardness* ≥ 520HV0,05
Bolt grades Up to A4-80
Temperature range*** -160°C to 500°C
Product designation NLss
NLspss
Laser marking type code SS

 

* In order to assure the unique mechanical locking function of the Nord-Lock washers, the hardness of the mating surfaces must be lower than the hardness of the Nord-Lock washers. 

** PREN (Pitting Resistance Equivalent Number) = %Cr + 3,3x%Mo + 16x%N. Figures in table valid for base material.

*** Temperature recommendations based on information from the raw material supplier and from tests. Locking function not affected within the specification.

Nord-Lock 254 SMO® Washers

Applications Corrosive environment – chloride rich environments, offshore, pumps, heat exchangers, nuclear, food, medical, processing
Material standard EN 1.4547
Size range M3-M39
#5 to 1 1/2"
Corrosion resistance PREN 45**
Hardening Surface hardened
Washer hardness* ≥ 600HV0,05
Bolt grades Up to A4-80
Temperature range*** -160°C to 500°C
Product designation NLss-254
NLspss-254
Laser marking type code 254

 

* In order to assure the unique mechanical locking function of the Nord-Lock washers, the hardness of the mating surfaces must be lower than the hardness of the Nord-Lock washers. 

** PREN (Pitting Resistance Equivalent Number) = %Cr + 3,3x%Mo + 16x%N. Figures in table valid for base material.

*** Temperature recommendations based on information from the raw material supplier and from tests. Locking function not affected within the specification.

 

Nord-Lock Alloy C-276 Washers

Applications Acidic environment – chemical industry, evaporators, offshore, downhole tooling
Material standard EN 2.4819 or equivalent
Size range M4-M20
#8 to 1 1/2"
Corrosion resistance PREN 68**
Hardening Surface hardened
Washer hardness* ≥ 520HV0,05
Temperature range*** -160°C to 500°C
Product designation NLss-276
NLspss-276
Laser marking type code 276

 

* In order to assure the unique mechanical locking function of the Nord-Lock washers, the hardness of the mating surfaces must be lower than the hardness of the Nord-Lock washers. 

** PREN (Pitting Resistance Equivalent Number) = %Cr + 3,3x%Mo + 16x%N. Figures in table valid for base material.

*** Temperature recommendations based on information from the raw material supplier and from tests. Locking function not affected within the specification.

Nord-Lock Alloy 718 Washers

Applications High temperatures – gas turbines, turbo charges, incinerators
Material standard EN 2.4668 or equivalent
Size range M4-M20
#5 to 1 1/2"
Corrosion resistance PREN 29**
Hardening Surface hardened
Washer hardness* ≥ 620HV0,05
Temperature range*** -160°C to 700°C
Product designation NLss-718
NLspss-718
Laser marketing type code 718

 

* In order to assure the unique mechanical locking function of the Nord-Lock washers, the hardness of the mating surfaces must be lower than the hardness of the Nord-Lock washers. 

** PREN (Pitting Resistance Equivalent Number) = %Cr + 3,3x%Mo + 16x%N. Figures in table valid for base material.

*** Temperature recommendations based on information from the raw material supplier and from tests. Locking function not affected within the specification.

All types of Nord-Lock washers

Material type
Steel Stainless
steel (ss)
254 SMO® ALLOY 
C-276
ALLOY
718
Applications
General steel applications General stainless steel applications Corrosive environment – chloride rich environments, offshore, pumps, heat exchangers, nuclear, food, medical, processing Acidic environment – chemical industry, evaporators, offshore, downhole tooling High temperatures – gas turbines, turbo charges, incinerators
Material standard
EN 1.7182 EN 1.4404 EN 1.4547 EN 2.4819 or equivalent EN 2.4668 or equivalent
Size range

M3-M130

#5 to 5"

M3-M80

#5 to 3 1/8"

M3-M39

#5 to 1 1/2"

M4-M20

#8 to 1 1/2"

M4-M20

#5 to 1 1/2"

Corrosion resistance
Minimum 1,000 hours in salt spray test (according to ISO 9227) PREN 27** PREN 45** PREN 68** PREN 29**
Hardening
Through hardened Surface hardened Surface hardened Surface hardened Surface hardened
Washer hardness*
≥ 465HV1 ≥ 520HV0,05 ≥ 600HV0,05 ≥ 520HV0,05 ≥ 620HV0,05
Coating
Delta Protekt® KL100 zinc flake coating - - - -
Bolt grades
Up to 12.9 Up to A4-80 Up to A4-80 Up to A4-80 Up to A4-80
Temperature range***
-50°C to 200°C -160°C to 500°C -160°C to 500°C -160°C to 500°C -160°C to 700°C
Product designation
NL
NLsp
NLss
NLspss
NLss-254
NLspss-254
NLss-276
NLspss-276
NLss-718
NLspss-718
Laser marking type code
flZn SS 254 276 718

 

* In order to assure the unique mechanical locking function of the Nord-Lock washers, the hardness of the mating surfaces must be lower than the hardness of the Nord-Lock washers. 

** PREN (Pitting Resistance Equivalent Number) = %Cr + 3,3x%Mo + 16x%N. Figures in table valid for base material.

*** Temperature recommendations based on information from the raw material supplier and from tests. Locking function not affected within the specification.

Výběr materiálu podložek

Parametr aplikace
Ocel Nerezová ocel (ss) 254 SMO® ALLOY 
C-276
ALLOY
718
Typ oceli
Materiál podle EN 1.7182  Materiál podle EN 1.4404  Materiál podle EN 1.4547  Materiál podle EN 2.4819 nebo ekvivalentní Materiál podle EN 2.4668 nebo ekvivaletní
Příklady aplikací
Všeobecné ocelové aplikace Všeobecné nerezové aplikace. Bezchlorové / kyselé prostředí Všeobecné aplikace pro užití se slanou vodou nebo ve slaném prostředí, čerpadla, aplikace pro atmosféry bohaté na chlorid, výměníky tepla, jaderné aplikace, odsolování, zařízení pro zpracování potravin a zdravotnická zařízení Všeobecná kyselá prostředí, procesní a chemický průmysl, odpařovací přístroje, nástrojové vybavení mimopevninských aplikací Aplikace operující ve vysokých teplotách, plynové turbíny, turbo dmychadla, spalovací pece
Dostupné pro velikosti šroubů

M3-M130

#5 - 5"

M3-M80

#5 - 3 1/8"

M3-M39

#5 - 1 1/2"

M3-M39 na poptávku

#5 - 1 1/2" na poptávku

M3-M39 na poptávku

#5 - 1 1/2" na poptávku

Typy podložek

Standardní vnější průměr (NL3 - NL130)

Zvětšený vnější průměr (NL3,5sp - NL36sp)

Standardní vnější průměr (NL3ss - NL80ss)

Zvětšený vnější průměr (NL3,5spss - NL30spss)

Standardní vnější průměr (NL3ss-254 - NL39ss-254)

Zvětšený vnější průměr (NL3,5spss-254 - NL27spss-254)

Standardní vnější průměr (NL3ss-276 - NL39ss-276)

Zvětšený vnější průměr (NL3,5spss-276 - NL27spss-276)

Standardní vnější průměr (NL3ss-718 - NL39ss-718)

Zvětšený vnější průměr (NL3,5spss-718 - NL27spss-718)

Povrchová úprava
Prokalené Delta Protekt® základní vrstva (KL100) a povrchová vrstva (VH302GZ) Povrchově kalené Povrchově kalené Povrchově kalené Povrchově kalené
Tvrdost podložek*
≥ 465HV1 ≥ 520HV0,05 ≥ 600HV0,05 ≥ 520HV0,05 ≥ 620HV0,05
Odolnost vůči korozi
Zkouška v solné komoře (podle IS09227) – v solné mlze vydrží minimálně 1,000 hodin PREN 27** PREN 45** PREN 68** PREN 29**
Pevnostní třídy šroubů
Až do 12.9 Až do A4-80 Až do A4-80 Až do A4-80 Až do A4-80
Teplotní rozsah***
-50°C až 200°C -160°C až 500°C -160°C až 500°C -160°C až 500°C -160°C až 700°C

 

* Pro zajištění správné funkčnosti podložek Nord-Lock musí být tvrdost povrchu základního materiálu nižší než je tvrdost podložek Nord-Lock (viz. tabulka výše). 

** PREN (Pitting Resistance Equivalent Number - index odolnosti proti bodové /pittingové/ korozi) = %Cr + 3,3x%Mo + 16x%N. Čísla v tabulce platná pro základní materiál.

*** Teplotní doporučení založena na informacích od dodavatele suroviny. Zajišťovací funkce není v rámci specifikace ovlivněna.

Tvrdost podložek

Pro zajištění jedinečné mechanické zajišťovací funkce podložek Nord-Lock, musí být tvrdost spojovaných povrchů nižší než tvrdost podložek Nord-Lock.


Typ podložky Velikost Povrchová úprava se zinkovými lamelami flZnnc – 600 Bez povrchové úpravy
Ocelové podložky (Through hardened) NL3 - NL42
NL45 - NL130
≥ 465 HV1
≥ 465 HV1
 
 Nerezové podložky (Surface hardened) NL3ss - NL80ss   ≥ 520 HV0.05
Podložky SMO 254® NL3ss-254 - NL80ss-254   ≥ 600 HV0.05


Tabulka pro převod tvrdosti

Vickers
HV
Brinell
HB
Rockwell
HRC
Rockwell
HRA
Šroub 8.8 Šroub 10.9 Šroub 12.9
300 285 29,8 65,5 |    
310 295 31,0 65,8 |    
320 304 32,2 66,4 | 320 HV  
330 314 33,3 67,0 | |  
335 319 33,9 67,3 335 HV |  
340 325 34,4 67,6   |  
350 333 35,5 68,1   |  
360 342 36,6 68,7   |  
370 352 37,7 69,2   |  
380 361 38,8 69,8   380 HV  
385 366 39,3 70,1     385 HV
390 371 39,8 70,3     |
400 380 40,8 70,8     |
410 390 41,8 71,4     |
420 399 42,7 71,8     |
430 409 43,6 72,3     |
435 414 44,1 72,5     435 HV
440 418 44,5 72,8      
460 437 46,1 73,6      
480 (456) 47,7 74,5      
500 (475) 49,1 75,3      
520 (494) 50,5 76,1      
540 (513) 51,7 76,7      

Úspěšné aplikace zákazníků

Obraťte se na nás.

Více informací o tom, jak nakládáme s vašimi osobními údaji, naleznete v části Oznámení o ochraně osobních údajů.

Děkujeme, že jste se na nás obrátili.